| 245 | 00 | ▼aBi-Mo 酸化物의 ALKALI 浸出에 관하여 /▼d李相和 著 |
| 260 | ▼a부산:▼b東亞大學校 大學院,▼c1980 | |
| 300 | ▼a26 p.:▼b삽도;▼c26 cm. | |
| 502 | ▼a학위논문(석사)--▼b東亞大學校 大學院:▼c金屬工學專攻,▼d1980. 2 | |
| 520 | ▼b영문초록 : This study is to find out the mechanism by which reaction products form when the bismuth trioxide and molybdenum trioxide is sufficiently mixed with a mole ratio of 1 to 1 and then heated at various temperatures selected from the differntial thermal analyses. The results obtained from the experiment that these reaction products have been alkali-leached are summarised as follows; 1. The reaction products of the mixture of Bi_(2)O_(3) and MoO_(3)(mole ratio=1:1) for 500℃ are Bi_(2)MoO_(6), Bi_(4)MoO_(9) and α-Bi_(2)O_(3), whereas at above 670℃ the product obtained is identified to be Bi_(4)MoO_(9) by the reation Bi_(2)MoO_(6)+α-Bi_(2)O_(3)--- Bi_(4)MoO_(9). 2. At a temperature of 1000℃ which is above the melting point of Bi_(2)O_(3) there is not change in weight. In the temperature range of 800 ℃ to 1000℃ below the boiling point of MoO_(3), however, it is shown to be a decrease in weight by 80%. 3. The melting point of Bi_(4)MoO_(9) is found to be 950℃. The change in weight of Bi_(4)MoO_(9) formed by mixing MoO_(3) and Bi_(2)O_(3) is not shown because of the formation of the compound Bi_(4)MoO_(9). 4. The chemical reaction analysis has shown that one of the reasons why the leaching rate of roasted ores of MoS_(2) containing Bi is lowered can be explained by the fact that Bi_(2)MoO_(6) and Bi_(4)MoO_(9) are not soluble in a solution of NaOH under the condition of atomosperic pressure. | |
| 650 | ▼aBM산화물 | |
| 950 | ▼aFB | |
| 950 | ▼a비매품▼b￦3000▼c(추정가) |
Bi-Mo 酸化物의 ALKALI 浸出에 관하여
Material type
학위논문 동서
Title
Bi-Mo 酸化物의 ALKALI 浸出에 관하여
Author's Name
Publication
부산: 東亞大學校 大學院 1980
Physical Description
26 p: 삽도; 26 cm.
학위논문주기
학위논문(석사)-- 東亞大學校 大學院: 金屬工學專攻, 1980. 2
Keyword
영문초록 : This study is to find out the mechanism by which reaction products form when the bismuth trioxide and molybdenum trioxide is sufficiently mixed with a mole ratio of 1 to 1 and then heated at various temperatures selected from the differntial thermal analyses. The results obtained from the experiment that these reaction products have been alkali-leached are summarised as follows; 1. The reaction products of the mixture of Bi_(2)O_(3) and MoO_(3)(mole ratio=1:1) for 500℃ are Bi_(2)MoO_(6), Bi_(4)MoO_(9) and α-Bi_(2)O_(3), whereas at above 670℃ the product obtained is identified to be Bi_(4)MoO_(9) by the reation Bi_(2)MoO_(6)+α-Bi_(2)O_(3)- Bi_(4)MoO_(9). 2. At a temperature of 1000℃ which is above the melting point of Bi_(2)O_(3) there is not change in weight. In the temperature range of 800 ℃ to 1000℃ below the boiling point of MoO_(3), however, it is shown to be a decrease in weight by 80%. 3. The melting point of Bi_(4)MoO_(9) is found to be 950℃. The change in weight of Bi_(4)MoO_(9) formed by mixing MoO_(3) and Bi_(2)O_(3) is not shown because of the formation of the compound Bi_(4)MoO_(9). 4. The chemical reaction analysis has shown that one of the reasons why the leaching rate of roasted ores of MoS_(2) containing Bi is lowered can be explained by the fact that Bi_(2)MoO_(6) and Bi_(4)MoO_(9) are not soluble in a solution of NaOH under the condition of atomosperic pressure.
관련 URL
Holdings Information
Call no. : 559.7 이519B
RReservation
MMissing Book Request
CClosed Stack Request
IInter-Campus Loan
CPriority Cataloging
PPrint
| Registration no. | Call no. | Location Mark | Location | Status | Due for return | Service |
|---|---|---|---|---|---|---|
|
Registration no.
E0131340
|
Call no.
559.7 이519B
|
Location Mark
D
|
Location
부민학위논문실
|
Status
대출불가 (소장처별 대출 불가)
|
Due for return
|
Service
|
|
Registration no.
E0131341
|
Call no.
559.7 이519B =2
|
Location Mark
D
|
Location
부민학위논문실
|
Status
대출불가 (소장처별 대출 불가)
|
Due for return
|
Service
|