Carbon fiber composites have excellent properties and can be used in automobile, aircraft, rail transit and otherfields of lightweight, but Its price is very expensive. For reducing the cost and improving the comprehensive properties ofmaterials which contain carbon fiber composites and used in the fields mentioned above, carbon fiber (CF) and glass fiber(GF) were mixed to replace pure carbon fiber composites. Three different methods were used to treat the surface of carbonfiber (ultrasonic surface cleaning, liquid phase oxidation of concentrated nitric acid and ultrasonic combined concentratednitric acid oxidation) and different contents of silane coupling agent KH-550 (0 %, 0.2 %, 0.5 %, 1.0 %) were used to treatthe glass fiber, and the laminated plate was prepared by Vacuum Assisted Resin Transfer Molding (VARTM). The CF/GFhybrid composite laminates were prepared by combining the best surface treatment method and the best stacking scheme ofcarbon fiber and glass fiber. The tests of mechanical properties and the observation of SEM fracture morphology show that,the surface treatment of CF by ultrasonic combined concentrated nitric acid oxidation is the best; mechanical properties of GFreinforced composite were the best when surface treatment was carried out with 0.5 % silane coupling agent; Compared withthe untreated samples, the mechanical properties of CF/GF hybrid composite laminates after surface treatment wereimproved, the thickness and weight are reduced. Thus, the weight reduction and better performances were achieved.