Combustion synthesis and luminescence properties of Dy (III) activated NaBaBO3 phosphor for solid state lighting applications.
- Resource Type
- Article
- Authors
- Khan, Zamir; Khan, Z. S.; Ingale, N. B.; Omanwar, S. K.
- Source
- AIP Conference Proceedings. 2019, Vol. 2104 Issue 1, p030035-1-030035-6. 6p.
- Subject
- *SELF-propagating high-temperature synthesis
*LUMINESCENCE spectroscopy
*LUMINESCENCE
*PHOSPHORS
*X-ray powder diffraction
*EXCITATION spectrum
*SCANNING electron microscopy
- Language
- ISSN
- 0094-243X
Polycrystalline samples of NaBaBO3:Dy3+ were prepared by employing modified solution combustion synthesis method. The phase formation was confirmed by X-ray powder diffraction (XRD) measurements. The prepared sample was characterized by using SEM and FTIR Techniques. The photoluminescence excitation and emission spectra were measured on HITACHI F-7000 fluorescence spectrometer. Under the excitation of near-UV light, Dy3+ doped NaBaBO3 presents the PLE spectra show the excitation peaks from 300 to 400 nm is due to the 4f–4f transitions of Dy3+. This mercury-free excitation is useful for solid state lighting and light-emitting diodes. The emission of Dy3+ ions upon 350 nm excitation is observed at 482 nm due to the 4F9/2→6H15/2 transitions and 574 nm due to 4F9/2→6H13/2 transitions. The CIE chromaticity coordinates for NaBaBO3:Dy3+ phosphors are simulated and located in the bluish-white region. The phosphor shows an excellent thermal stability on temperature quenching effects. The effect of concentration of Dy3+ ions on the PL intensity has also been investigated. It has been observed that the powder sample exhibits highest PL emission intensity for Dy3+ concentration of about 0.01 moles. The results were discussed on the relationship between the structure and the luminescence properties. [ABSTRACT FROM AUTHOR]