| 245 | 00 | ▼a酸素 雰圍氣가 TiO2 薄膜 素子에 미치는 影響에 관한 硏究/▼d韓進玉 |
| 260 | ▼a부산:▼b東亞大學校,▼c1982 | |
| 300 | ▼a26p.:▼b삽도;▼c26cm | |
| 502 | ▼a학위논문(석사)▼b東亞大學校 大學院:▼c電子工學科,▼d1982 | |
| 520 | ▼b영문초록 : Al-TiO2-Al sandwich type thin films are fabricated by the vacuun evaporation, and they are made as annealed samples (under oxygen atmosphere) and unannealed ones. Measurements are carried out for dielectric constant ε', dielectric loss ε" , and loss factor (tan δ) with the variation of frequency. The experimental results are as follows , 1. The produced capacitor shows dielectric constant 60-105 at frequency lKHZ and capacitance 1500-2500pF. 2. When annealed under oxygen atmosphere , the values of dielectric constant and capacitance of the capacitor increases with the period of annealing time. 3. It can be confirmed through experiment that the annealed sample under oxygen atmosphere has larger values of dielectric constant and capacitance. 4. It can be said that the produced sample with this procedure could be used as a thin film capacitor. | |
| 650 | ▼a박막▼x전자공학 | |
| 856 | ▼adonga.dcollection.net▼uhttp://donga.dcollection.net/jsp/common/DcLoOrgPer.jsp?sItemId=000002145395 | |
| 950 | ▼aFB | |
| 950 | ▼a비매품▼b￦3,000▼c(추정가) |
酸素 雰圍氣가 TiO2 薄膜 素子에 미치는 影響에 관한 硏究
종류
학위논문 동서
서명
酸素 雰圍氣가 TiO2 薄膜 素子에 미치는 影響에 관한 硏究
저자명
발행사항
부산: 東亞大學校 1982
형태사항
26p: 삽도; 26cm
학위논문주기
학위논문(석사) 東亞大學校 大學院: 電子工學科, 1982
주기사항
영문초록 : Al-TiO2-Al sandwich type thin films are fabricated by the vacuun evaporation, and they are made as annealed samples (under oxygen atmosphere) and unannealed ones. Measurements are carried out for dielectric constant ε', dielectric loss ε" , and loss factor (tan δ) with the variation of frequency. The experimental results are as follows , 1. The produced capacitor shows dielectric constant 60-105 at frequency lKHZ and capacitance 1500-2500pF. 2. When annealed under oxygen atmosphere , the values of dielectric constant and capacitance of the capacitor increases with the period of annealing time. 3. It can be confirmed through experiment that the annealed sample under oxygen atmosphere has larger values of dielectric constant and capacitance. 4. It can be said that the produced sample with this procedure could be used as a thin film capacitor.
관련 URL
소장정보
청구기호 : 569 한79산
예도서예약
서서가부재도서 신고
보보존서고신청
캠캠퍼스대출
우우선정리신청
검검색지인쇄
| 등록번호 | 청구기호 | 별치기호 | 소장위치 | 대출상태 | 반납예정일 | 서비스 |
|---|---|---|---|---|---|---|
|
등록번호
E0182606
|
청구기호
569 한79산
|
별치기호
D
|
소장위치
부민학위논문실
|
대출상태
대출불가 (소장처별 대출 불가)
|
반납예정일
|
서비스
|
|
등록번호
E0182607
|
청구기호
569 한79산 =2
|
별치기호
D
|
소장위치
부민학위논문실
|
대출상태
대출불가 (소장처별 대출 불가)
|
반납예정일
|
서비스
|
|
등록번호
E0535770
|
청구기호
569 한79산 =3
|
별치기호
D
|
소장위치
부민학위논문실
|
대출상태
대출불가 (소장처별 대출 불가)
|
반납예정일
|
서비스
|