The mechanical behavior of a composite with thermoplastic matrix and glass fiber reinforcement has been studied. It has been tested to constant stresses of a value equivalent to tensile strength divided by three to 50, 100 and 150 ºC, during periods of time between 250 and 3000 minutes. A decrement of the tensile strength and deformation can be observed in the three temperatures. Also a group of specimens have been exposed to accelerated aging in an environmental chamber to 70 ºC and 95% RH, during 30 days; and after they have been tested. In that case a decrement of the strength and deformation after 250 minutes has been observed, but in larger time of exposure these properties suffered an increment.Se ha estudiado el comportamiento mecánico de un compuesto fabricado con un termoplástico PEI (polieterimida) reforzado con tejido de fibra de vidrio, frente a ensayos en los que se mantienen tensiones iguales a un tercio de su resistencia a tracción a 50, 100 y 150 ºC, durante periodos comprendidos entre 250 y 3000 minutos. En los resultados se observa una disminución de la resistencia y de la deformación en las tres temperaturas, con un mantenimiento de sus valores hasta las ensayadas a 3000 minutos. Además fueron expuestas un grupo de probetas del material, a envejecimiento acelerado en cámara higrotérmica a 70 ºC y a un 95% de H.R., durante 30 días; para luego someterlas a los ensayos antes descritos. Para esas probetas se obtuvieron pequeñas fluctuaciones de la resistencia y deformación con el tiempo, sin observarse una influencia significativa de la temperatura a la que se hicieron los ensayos termomecánicos.