Abstract: BaCe0.8Sm0.1Gd0.1O3−δ , a material for an electrolyte of solid oxide fuel cells, was prepared by a newly sol-combustion method to obtain fine grain size and good sinterability. The phase formation, sinterability and electrical conductivity were focused on by this study. The results show that nano-sized BaCe0.8Sm0.1Gd0.1O3−δ powders with single orthorhombic perovskite structure were prepared by this process successfully. The powders showed high sinterability, and a relative of 95.2% of the theoretical density was obtained at a sintering temperature of 1400°C. Electrochemistry measurements showed that the BaCe0.8Sm0.1Gd0.1O3−δ ceramics had relatively high oxygen ionic conductivity in low-temperature range. [Copyright &y& Elsevier]