Currently in Korea, as a part of the lack of natural aggregates and recycling construction waste, the government has strongly recommended the use of recycled aggregates. If the natural aggregates are replaced with recycled aggregates, not only would it be possible to increase economic value but also eliminate the difficulties in supply of the natural aggregates.Crushed waste concretes become good-quality recycled aggregates at the end of several processes such as removing rebar, foreign substances and the 3 or 4 step crushing process. Residual mortar content which is attached to the recycled aggregates is varied in accordance with the crushing step. Moreover this varying the residual mortar content will act as a factor influencing physical properties of concrete to be produced. The residual mortar content also has a negative association with the physical properties mostly. The Equivalent Mortar Volume Mixture Design method has been developed abroad which is considering the residual mortar as new mortar to be newly added. Therefore, it is possible to enhance economic feasibility by reducing cement and fine aggregates, which are included in the residual mortar. Moreover, the properties for recycled aggregate concrete can be improved with the natural aggregates concrete level.In this study, the residual mortar affecting the properties of recycled aggregate concrete and alkali-silica reactivity before and after removing the residual mortar are assessed to verify effectiveness of the Equivalent Mortar Volume Mixture Design method. Moreover, the relationship between mortar volume and properties for concrete are analyzed through comparing compressive strength and modulus of elasticity, which are from two types of concrete; one is Equivalent Mortar Volume Mixture Design method and the other one is Conventional Mixture Design method.Test results show that the residual mortar which is in Conventional Mixture Design work as a factor lowering the alkali-silica reactivity and physical properties such as compressive strength and modulus of elasticity. However in the case of the Equivalent Mortar Volume Mixture Design method, which contains constant total mortar volume, irrespective of the residual mortar content of recycled aggregates, validation can be ascertained due to property degradation not being observed.
현재 국내에서는 천연골재의 부족과 건설폐기물 재활용의 일환으로 순환골재의 사용을 국가적 차원에서 적극 권장․규제 하고 있다. 천연골재를 순환골재로 대체할 경우, 천연골재 수급의 어려움을 해소하고, 건설폐 기물 재활용에 따른 경제적 부가가치를 창출할 수 있다.파쇄된 폐콘크리트는 철근 및 이물질 제거, 크러셔를 통한 3~4단계의 파쇄 공정 끝에 양질의 순환골재로 변모하게 된다. 순환골재에 부착되어 있는 잔류 모르타르는 파쇄 단계에 따라 그 함량이 변하게 되는데, 이때 변화되는 잔류 모르타르의 함량은 향후 제작될 콘크리트의 물성을 좌우하는 요인으로 작용하게 되며, 대개 잔류 모르타르 함량과 물성은 반비례 관계를 가진다. 이에 국외에서는 잔류 모르타르를 골재가 아닌 신규 투입될 모르타르로 간주하는 ‘등가 모르타르 체적 배합설계법’이 개발되었으 며, 이를 통하여 잔류 모르타르 함량만큼 추가되는 시멘트와 잔골재를 줄일 수 있어 경제성을 도모할 수 있고, 순환골재 콘크리트의 물성 또한 천연골재 콘크리트 수준으로 향상 시킬 수 있다고 하였다.따라서 본 연구에서는 잔류 모르타르가 콘크리트의 물성에 미치는 영향을 평가하고 등가 모르타르 체적 배합설계법의 효용성 검증을 위해 잔류 모르타르 제거 전․후의 순환골재를 이용하여 알칼리-실리카 반응성을 평가하고, 등가 모르타르 체적 배합설계법과 기존의 일반 콘크리트 배합 설계법을 사용한 콘크리트의 압축강도, 탄성계수 비교를 통해 콘크리트를 구성하는 모르타르 부피와 물성과의 관계를 분석하였다.실험 결과, 잔류 모르타르는 골재의 알칼리-실리카 반응성, 일반 콘크리 트의 압축강도 및 탄성계수에 있어서 물성을 저하시키는 요인으로 작용하 였으나, 잔류 모르타르 함량에 관계없이 전체 모르타르의 부피를 일정하게 제어하는 등가 모르타르 체적 배합설계법 기반의 콘크리트에서는 물성 저하가 관찰되지 않아 그 효용성을 확인 할 수 있었다.