It has been reported that the addition of graphene oxide (GO) can increase the dispersion and heterogeneousnucleation of layered double hydroxide (LDH), thus providing more active sites, which is more conduciveto CO2 adsorption. Herein, we reported alkali metal nitrates ((Li0.3Na0.18K0.52)NO3) promoted LDHand GO composites (LDH/GO) as adsorbents for CO2 capture. The influence of mass ratio of LDH to GO, theimpregnation ratio of alkali metal nitrates, the calcination and adsorption temperature, as well as thecycling stability were investigated systematically. The results indicated that the CO2 capture capacityof LDH/GO composite with 30 mol% (Li0.3Na0.18K0.52)NO3 could reach 4.51 mmol g 1, which was 5.86times higher than LDH/GO1 without loading alkali metal nitrates. Moreover, it had outstanding CO2adsorption capacity in the range from 200 C to 320 C. In addition, the cyclic adsorption and desorptiontest manifested that the CO2 uptake of the material can reach 3.07 mmol g 1 after 22 cycles. We believethat this study will give a significant contribution to fabrication of LDH based composites as CO2 adsorbentsin future study.