With the widespread development of sponge city projects across the country, the use of industrial permeable bricks hasincreased dramatically. My country produces a large amount of refractory waste and pollutes the environment seriously. Wasterefractory insulation bricks are used as the main raw materials, and a small amount of auxiliary raw materials are added toprepare sponge urban permeable bricks through forming and sintering processes. Through performance tests, such asporosity, flexural strength, and water permeability coefficient, the effect of process parameters on the performance ofpermeable bricks is studied, the process parameters of using refractory waste are comprehensively optimized to preparesponge urban permeable bricks, and permeable bricks are prepared for the industrialization of high-quality industrial solidwaste. Brick provides reference. Through the experimental results and analysis, the following conclusions are drawn: the rawmaterial ratio of refractory brick waste: binder: foaming agent: sintering aid is 80:10:1:9. Slurry water mill foaming occurswhen the water to material ratio is 0.5, the ball milling speed is 80 r/min, and the ball milling time is 2 h; the foaming effectand molding performance are better. In the drying stage, drying at 45 oC for 12 h has the best molding effect. The sinteringsystem at 1,300 oC and holding time of 1 h has the best sintering performance. After optimizing the process, the porosity ofthe permeable bricks can reach 48.4%, the water permeability coefficient is 2.1×10^-2 cm/s, the national permeable brick hasA-level standard, and the compressive strength is 26.8 MPa.