The Mechanical Resistance of Asphalt Mixture with Steel Slag to Deformation and Skid Degradation Based on Laboratory Accelerated Heavy Loading Test
- Resource Type
- article
- Authors
- Jiasheng Li; Jianying Yu; Shaopeng Wu; Jun Xie
- Source
- Materials, Vol 15, Iss 3, p 911 (2022)
- Subject
- asphalt mixture
steel slag
heavy loading
aggregate analysis
permanent deformation
skid resistance
Technology
Electrical engineering. Electronics. Nuclear engineering
TK1-9971
Engineering (General). Civil engineering (General)
TA1-2040
Microscopy
QH201-278.5
Descriptive and experimental mechanics
QC120-168.85
- Language
- English
- ISSN
- 15030911
1996-1944
Steel slag is a main form of solid waste. Using this component to replace part of the aggregate in an asphalt mixture is an effectively way of treating solid waste. To study the performance degradation of asphalt mixture with various content of steel slag under heavy loading, some large-sized basalt hot mixed asphalt mixture (BHMA) and steel slag hot mixed asphalt mixture (SHMA) in a form of specimens were prepared and a heavy loading wheel tracking test was conducted. The aggregate characteristics of basalt and steel slag were measured. The deformation and skid resistance of the asphalt mixture with different content of steel slag was tested and analyzed. Due to the particle characteristics of steel slag aggregate, it was found that a low content of steel slag can effectively improve the resistance to deformation and skid resistance of the asphalt mixture under heavy loading. The response of SHMA can still meet the pavement technical requirement after long-term heavy loading service. The main change in the mixture under heavy loading is the crushing of the 9.5–16 mm aggregate, and the content of this part also significantly affects the deformation. This study explains the mechanism of degradation of SHMA under heavy loading: the large aggregate is crushed and forms a new aggregate skeleton structure.