We review the salient features of two advanced nodes of an 8-Nb-layer fully planarized process developed recently at MIT Lincoln Laboratory for fabricating Single Flux Quantum(SFQ) digital circuits with very large scale integration on 200-mm wafers: the SFQ4ee and SFQ5ee nodes, where 'ee' denotes the process is tuned for energy efficient SFQ circuits. The former has eight superconducting layers with 0.5 {\mu}m minimum feature size and a 2 {\Omega}/sq Mo layer for circuit resistors. The latter has nine superconducting layers: eight Nb wiring layers with the minimum feature size of 350 nm and a thin superconducting MoNx layer (Tc ~ 7.5 K) with high kinetic inductance (about 8 pH/sq) for forming compact inductors. A nonsuperconducting (Tc < 2 K) MoNx layer with lower nitrogen content is used for 6 {\Omega}/sq planar resistors for shunting and biasing of Josephson junctions. Another resistive layer is added to form interlayer, sandwich-type resistors of m{\Omega} range for releasing unwanted flux quanta from superconducting loops of logic cells. Both process nodes use Au/Pt/Ti contact metallization for chip packaging. The technology utilizes one layer of Nb/AlOx-Al/Nb JJs with critical current density, Jc of 100 {\mu}A/{\mu}m^2 and minimum diameter of 700 nm. Circuit patterns are defined by 248-nm photolithography and high density plasma etching. All circuit layers are fully planarized using chemical mechanical planarization (CMP) of SiO2 interlayer dielectric. The following results and topics are presented and discussed: the effect of surface topography under the JJs on the their properties and repeatability, critical current and Jc targeting, effect of hydrogen dissolved in Nb, MoNx properties for the resistor layer and for high kinetic inductance layer, technology of m{\Omega}-range resistors.
Comment: 10 pages, 12 figures, 1 table, 27 references. The paper was presented on September 8, 2015 at the 12th European Conference on Applied Superconductivity, EUCAS 2015, 6-10 September 2015, Lyon, France, IEEE Transaction on Applied Superconductivity, 2016