Water vapour permeability of poly(lactic acid): Crystallinity and the tortuous path model.
- Resource Type
- Article
- Authors
- Duan, Z.; Thomas, N. L.
- Source
- Journal of Applied Physics. 2014, Vol. 115 Issue 6, p1-9. 9p. 3 Black and White Photographs, 1 Chart, 9 Graphs.
- Subject
- *WATER vapor
*PERMEABILITY
*POLYLACTIC acid
*LACTIC acid
*POLYMERS
- Language
- ISSN
- 0021-8979
The water vapour transmission rates (WVTR) through samples of polylactic acid of different crystallinities have been measured. Three different grades of commercial poly(lactic acid) (PLA) were used with different ratios of L-lactide and D-lactide to give a range of crystallinities from 0% to 50%. Sheets of PLA were prepared by melt compounding followed by compression moulding and annealing at different temperatures and for different times to give the range of crystallinities required. Crystallinity was measured by differential scanning calorimetry and the morphology of the samples was observed under crossed polars in a transmitted light microscope. Water vapour transmission rates through the films were measured at 38ºC and at a relative humidity of 90%. It was found that the measured values of WVTR decreased linearly with increasing crystallinity of the PLA from 0% to 50%. The results are discussed in terms of the effect of crystallinity on solubility and shown to ?t the "Tortuous Path Model." The model was also successfully used to explain published data on water permeability of polyethylene terephthalate. [ABSTRACT FROM AUTHOR]