Control of thermal expansion (TE) is important to improve material longevity in applications with repeated temperature changes or fluctuations. The TE behavior of metal-organic frameworks (MOFs) is increasingly well understood, while the impact of surface-mounted nanoparticles (NPs) on the TE properties of MOFs remains unexplored despite large promises of NP@MOF composites in catalysis and adsorbate diffusion control. Here we study the influence of surface-mounted platinum nanoparticles on the TE properties of Pt@MOF (Pt@Zn2(DP-bdc)2dabco; DP-bdc2-=2,5-dipropoxy-1,4-benzenedicarboxylate, dabco=1,4-diazabicyclo[2.2.2]octane). We show that TE is largely retained at low platinum loadings, while high loading results in significantly reduced TE at higher temperatures compared to the pure MOF. These findings support the chemical intuition that surface-mounted particles restrict deformation of the MOF support and suggest that composite materials exhibit superior TE properties thereby excluding thermal stress as limiting factor for their potential application in temperature swing processes or catalysis. Controlling the thermal expansion of a material is of importance for material longevity in applications with fluctuating temperatures. Here, the impact of nanoparticle loading on the thermal expansion behaviour of a pillared metal–organic framework is explored using variable temperature powder X-ray diffraction, and a significant reduction in the thermal stress is observed. [ABSTRACT FROM AUTHOR]