Abstract: Using the current-voltage measurements, we observed the barrier heights of c-plane GaN in Pt and Au Schottky contacts to be higher than those of a-plane GaN. However, the barrier height of c-plane GaN was lower than that of a-plane GaN in the Ti Schottky contacts. The N/Ga ratio calculated by integrating the X-ray photoelectron spectroscopy (XPS) spectra of Ga 3d and N 1s core levels showed that c-plane GaN induced more Ga vacancies near the interface than a-plane GaN in the Ti Schottky contacts, reducing the effective barrier height through an enhancement of the tunneling probability.