Triplex particulate composites composed of boride and carbide ceramics were found to have high strength, hardness, and fracture toughness values. Two compositions consisting of 70:15:15 and 1:1:1 volume ratios of TiB2, SiC, and B4C were produced from commercially available powders by hot-pressing. The 70:15:15 ceramic exhibited a strength of ~1.3 GPa, while the 1:1:1 ceramic had a strength of ~0.9 GPa. These strengths are comparable to super-strong Y2O3-PSZ and β-SiAlON based composites. The Vickers' hardness values of these ceramics were ~32 GPa for indent loads of 9.8 N. Hardness increased as indentation load decreased. The 1:1:1 ceramic had a hardness of ~53 GPa at an indentation load of 0.49 N, higher than values reported for so-called "super-hard" ceramics, and comparable to c-BN. [ABSTRACT FROM AUTHOR]